| 特性 TypicalProperties | 測試方法 ISO | 測試條件 Condition | 單位 Units | 一 般 級 | 食品接觸級 | ||||||
| PN-108 | PN-118 | PN-128 | PN-138H | D-168 | D-178 | D-178HF | PN-107FG | ||||
| 熔體流動速率 MVR | 1133 | 200℃x5kg | ml/10min | 5.0 | 2.8 | 3.0 | 1.0 | 1.0 | 2.7 | 17.0 | 5.2 |
| 220℃x10kg | 51.0 | 34.0 | 35.0 | 11.0 | 11.0 | 30.0 | 183.0 | 58.0 | |||
| 質量密度 Mass Density | 1183 | 23℃ | g/cm3 | 1.07 | 1.07 | 1.07 | 1.08 | 1.08 | 1.07 | 1.07 | 1.06 |
| 拉伸強度 TensileStrength | 527 | 50mm/min | MPa | 67.0 | 71.0 | 72.0 | 81.0 | 81.0 | 75.0 | 57.0 | 65.0 |
| 延伸率Tensile Elongation | 527 | 50mm/min | % | 5.0 | 5.0 | 5.0 | 7.0 | 7.0 | 5.0 | 4.0 | 4.0 |
| 彎曲強度 FlexuralStrength | 178 | 2mm/min | MPa | 101 | 106 | 110 | 124 | 124 | 115 | 75 | 89 |
| 彎曲彈性模數 FlexuralModulus | 178 | 2mm/min | GPa | 3.4 | 3.4 | 3.6 | 3.7 | 3.7 | 3.5 | 3.4 | 2.6 |
| IZOD沖擊強度 Izod Impact | 180 | 23℃ Notched | kJ/m2 | 3.8 | 3.8 | 3.9 | 4.0 | 4.0 | 3.8 | 3.7 | 2.0 |
| Charpy沖擊強度 CharpyImpact | 179 | 23℃ Notched | kJ/m2 | 2.7 | 2.7 | 2.7 | 2.8 | 2.8 | 2.7 | 2.6 | 2.0 |
| 維氏軟化溫度 Vcat Softening Temp. | 306 | 50℃/Hr | ℃ | 105 | 105 | 107 | 108 | 108 | 105 | 104 | 104 |
| 熱變形溫度 HeatDefiection Temp. | 75-2 | unannealed | ℃ | 86 | 86 | 88 | 89 | 89 | 87 | 85 | 88 |
| annealed | ℃ | 97 | 97 | 99 | 100 | 100 | 97 | 98 | 99 | ||
| 燃燒性 Flammability | - | UL-94 | - | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB |
| 產品特性與應用 | 一般射出 L100:本色 L125:極淡藍 | 一般射出 L100:本色 L150:淡藍 | 一般射出 L100:本色 L150:淡藍 | 高強度 高耐化性 | 高強度 高耐化性 | 中強度耐化性 | 高流動級 | 食品接觸級L125：極淡藍 | |||